1.75 G/Cm3 High Temperature Vacuum Furnace Graphite CFC Box

Certification
China Qingdao Jiacheng Graphite Products Co., Ltd. certification
I'm Online Chat Now

1.75 G/Cm3 High Temperature Vacuum Furnace Graphite CFC Box

1.75 G/Cm3 High Temperature Vacuum Furnace Graphite CFC Box
1.75 G/Cm3 High Temperature Vacuum Furnace Graphite CFC Box 1.75 G/Cm3 High Temperature Vacuum Furnace Graphite CFC Box

Large Image :  1.75 G/Cm3 High Temperature Vacuum Furnace Graphite CFC Box

Product Details:
Place of Origin: Qingdao
Brand Name: JC
Certification: JC
Payment & Shipping Terms:
Minimum Order Quantity: 1
Price: negotiable
Packaging Details: wooden box
Delivery Time: 5-8 work days
Payment Terms: T/T
Supply Ability: 5000PC

1.75 G/Cm3 High Temperature Vacuum Furnace Graphite CFC Box

Description
Material: Foreign Graphite Size: Customize
Package: Wooden Box Deliver Time: 5-8 Work Days
Port: Qingdao Port Brand: JC
High Light:

1.75 g cm3 Vacuum Furnace Graphite

,

1.75 g cm3 composite graphite

,

CFC Vacuum Furnace Graphite

CFC Box C/C Material For High Temperature And Vacuum Furnaces

 

Product description:

Our Carbon Carbon Composite ( C/C) or carbon fiber-reinforced carbon ( CFC) products are made of 2.5D carbon fiber fabric. Material density is 1.3-1.75 g/cm3, the compressive strength greater than 190 MPa, and flexural strength greater than 140 MPa, Tensile strength greater than 100 MPa. It can be used in vacuum furnace under the temperature of 2500 centigrade degrees. The biggest size is up to 1400*1400mm
All the machining products of Carbon Carbon Composite including plate, bolt, nut and screw are machined by CNC machine with exact size. Under the conditions of normal use, the service life is not less than 18 months.

 

We can machine various types of CFC Box according to customers' designs.

The carbon / carbon composites (C/C) is a material composed of high strength carbon fibers and carbonized base reinforced through a graphitization process. It can be widely used as various components, heaters and containers in high temperature environment. Compared with traditional engineering materials, C/C has the following advantages: High strength (5 times that of steel at high temperature), High temperature resistance ( maintaining excellent mechanical and electrical performance at 2,000 °C), Excellent thermal shock resistance, low thermal expansion coefficient, low thermal capacity, low density and excellent corrosion and radiation resistance.

 

The main field of application:

Parts of CZ,Parts of high temperature furnace

Fastener or connect of high temperature furnace
Heater
All kinds of high-temperature container

 

 

 

CFC Box C/C Material For High Temperature And Vacuum Furnaces materials:

The carbon / carbon composites (C/C) is a material composed of high strength carbon fibers and carbonized base reinforced through a graphitization process. It can be widely used as various components, heaters and containers in high temperature environment.

 

Typical property Data

Characteristics unit JC-540 JC-740
Carbon fiber - short fiber short fiber
Heat treatment °C 2000 2000
Bulk density g/cm3 1.6 1.6
Flexural strength Mpa 170 170
Flexural modulus Gpa 40 40
Flexural modulus Mpa 150 190
Flexural modulus Gpa 50 50
Compressive strength Mpa 120// 120 130// 190
Coeffeciency of thermal expansion 10-6/º C 1.4// 10.5 0.9// 9.2
Thermal conductivity W/m*k 40// 10 40// 10
Specific heat J/Kg*k 750(25ºC)1970(1300ºC) 750(25ºC)
Porus % 18 18

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

* The given values are not authoritative , but are typical values from our experience.

Material and production-specific distribution is to be taken into account.

 
 
Graphite advantages:

Because of the high tempearture resistance, thermal conductivity, corrosion resistance and special thermal shock resistance, graphite is widely used in metallurgy, mechanical, electrial, chemical, textile, denfense and other industries.
1. High strength. As the temperature rises, the graphite strength increases
2. High temperature resistance
3. Good heat shock resistance
4. Anti-oxidation
5. Strong corrosion resistance to acid and alkali liquid
6. Good conductivity and thermal efficiency.
7. Excellent chemical stability
8. High heat conductivity
9. Mechanical shock resistance
10. Small thermal expansion coefficient

 

 

Production environment:

1.75 G/Cm3 High Temperature Vacuum Furnace Graphite CFC Box 0

1.75 G/Cm3 High Temperature Vacuum Furnace Graphite CFC Box 1

1.75 G/Cm3 High Temperature Vacuum Furnace Graphite CFC Box 2

1.75 G/Cm3 High Temperature Vacuum Furnace Graphite CFC Box 3

1.75 G/Cm3 High Temperature Vacuum Furnace Graphite CFC Box 4

1.75 G/Cm3 High Temperature Vacuum Furnace Graphite CFC Box 5

1.75 G/Cm3 High Temperature Vacuum Furnace Graphite CFC Box 6

Our company is the professional manufacturer and exporter for graphite products. our company was established at 2008.Our factory is located in Qingdao city. We believe that due to our high quality graphite material and formed graphite parts at very competitive prices with professional service,broad product knowledge and technical expertise can help you save much resource and improve your efficiency,and satisfy more of your customers' needs.

Contact Details
Qingdao Jiacheng Graphite Products Co., Ltd.

Contact Person: admin

Tel: +8618561388531

Send your inquiry directly to us (0 / 3000)